The basic requirements of rolling bearing steel


Posted January 7, 2015 by xinxinyy

Bearing under the action of cyclic load, the contact surface is easy to fatigue failure, namely appear cracked spalling

 
A, contact fatigue strength
Bearing under the action of cyclic load, the contact surface is easy to fatigue failure, namely appear cracked spalling, this is the main skf Bearings http://kvtca.fkq199.com/ damage forms.Therefore, in order to improve the service life of the bearing, bearing steel must have a high contact fatigue strength.
Second, the wear-resisting performance
Bearing work, not only between race, rolling element and cage rolling friction, and sliding friction will occur, so that the bearing parts wear continuously.To reduce the number of bearing parts wear, keep bearing accuracy stability, prolong the service life, bearing steel should have good wear resistance.
Three, hardness
Hardness is one of the important quality of Bearing skf http://unymf.fkq199.com/ quality, the contact fatigue strength, wear resistance, elastic limit has a direct impact.The hardness of bearing steel in the condition of using general to achieve HRC61 ~ 65, bearing can get high contact fatigue strength and wear resistance.
Fourth, rust resistance
In order to prevent bearing parts and finished products during processing, storage and use of corrosion rust, for bearing steel should have good rust resistance.
Five, the processing performance
Bearing parts in the process of production, after a lot of cold and hot working process, in order to meet the requirements of mass, high efficiency, high quality, bearing steel should have good processing performance.For example, the cold and hot forming properties, machinability, hardenability, etc.
Bearing steel in addition to the above basic requirements, should also reach the appropriate chemical composition, less uniform and internal organization, non-metallic inclusion, internal accord with a standard surface defect and surface decarburization layer does not exceed the prescribed concentration requirements, these projects are clearly defined in the standard of raw materials.
Bearing parts commonly used materials mainly include: high carbon chromium bearing steel, carburized steel (e.g., 20 cr2ni4a, 15 mn, 20 cr2mnmoa), high temperature bearing steel (such as Cr4Mo4V, Cr14Mo4 Cr15Mo4V W18Cr4V), stainless bearing steel cr18 (9, 9 cr18mo, 1 cr18ni9ti) magnetic, vacuum degassing steel, bearing steel, etc., one of the most commonly used is high carbon chromium bearing steel.Basic steel grade of high carbon chromium bearing steel are GCr6, GCr9, GCr9SiMn, GCr15, GCr15SiMn, it is the most widely used in bearing manufacturing industry in China, the amount of the largest steel, have good wear resistance and contact fatigue performance, has the ideal processing
-- END ---
Share Facebook Twitter
Print Friendly and PDF DisclaimerReport Abuse
Contact Email [email protected]
Issued By hrhrjjr
Country China
Categories Automotive , Design
Last Updated January 7, 2015